Niobium pentoxide Nb2O5 Evaporation Materials

Niobium pentoxide Nb2O5 Evaporation Materials

    Niobium pentoxide Nb2O5 Evaporation Materials

Application of Nb2O5 compounds in the laboratory and industry and steps for laboratory evaporation coating

Applications of Niobium Pentoxide (Nb2O5) Compounds

Niobium pentoxide (Nb2O5) is an important inorganic compound with a wide range of laboratory and industrial applications due to its excellent electrical, mechanical and chemical properties.

 

Laboratory applications:

Electrolytic capacitors: Nb2O5 is used in the manufacture of solid electrolytic capacitors with high dielectric constant and good electrical properties.

Catalyst: Nb2O5 is widely used as a catalyst in chemical reactions, in organic synthesis and petrochemicals.

Optoelectronic devices: Nb2O5 thin films are used in optoelectronic devices such as solar cells and photodetectors due to their excellent optical and electrical properties2.

Industrial applications:

Lithium-ion batteries: Nb2O5 is used as an anode material for lithium-ion batteries with high capacity and long cycle life.

Optical coatings: Nb2O5 is used to make anti-reflective coatings and optical filters due to its high refractive index and low absorption.

Superconducting materials: Nb2O5 is used in the manufacture of superconducting materials due to its excellent electrical conductivity1.

Ceramics and Glasses: Nb2O5 is used in the manufacture of high-performance ceramics and glasses to enhance the mechanical strength and heat resistance of the materials.

 

Detailed steps for laboratory evaporative coating

Preparation:

Substrate cleaning:

Ultrasonic cleaning: Use ultrasonic cleaner to remove oil and particles from the surface of the substrate.

Solvent Cleaning: Use a suitable solvent (e.g. ethanol or acetone) to further clean the substrate surface.

CY Plasma Cleaning: Plasma cleaning is performed using CY plasma cleaning equipment. Plasma cleaning removes organic contaminants and oxidized layers from the surface of the substrate by generating high-energy plasma to improve the hydrophilicity and adhesion of the substrate surface. The specific steps are as follows:

Load the substrate: Place the substrate on the sample table of the CY plasma cleaning equipment.

Vacuum extraction: Start the vacuum pump to extract the air from the cleaning chamber to reach the required vacuum level.

Plasma Cleaning: Start the plasma generator, select the appropriate gas (such as oxygen or argon), adjust the power and time for plasma cleaning.

Cooling and Removal: After the cleaning is completed, turn off the plasma generator and remove the substrate after it has cooled down.

Vacuum extraction:

Vacuum Chamber: Place the substrate and coating material in the vacuum chamber, use mechanical and molecular pumps to extract the air from the chamber to achieve a high vacuum (usually below 10^-6 Torr).

Heating for evaporation:

Resistance heating:

Installation of resistor wire: a resistor wire (e.g., tungsten wire) is installed on the evaporation source and the coating material is placed on the wire.

Heating: Electricity is applied to heat the resistance wire to gradually increase its temperature until the coating material begins to evaporate. Resistance heating is suitable for the evaporation of low melting point materials.

Temperature control: The temperature of the resistance wire is precisely controlled by adjusting the current and voltage to ensure uniform evaporation of the coating material.

Electron beam heating:

Installation of coating material: Place the coating material in the crucible of the electron beam evaporation source.

E-beam Generator: Start the E-beam generator, the electron beam is focused and accelerated by an electromagnetic field to impact the surface of the coating material.

Heating and Evaporation: The high energy of the E-beam causes the coating material to rapidly heat up and evaporate. E-beam heating is suitable for evaporation of high melting point materials.

Controlling the Electron Beam: By adjusting the power and scanning speed of the electron beam, the evaporation rate of the coated material is precisely controlled.

Deposition of the film:

Evaporation Diffusion: The evaporated material diffuses in a vacuum and condenses on the surface of the substrate to form a uniform film. By adjusting the temperature and position of the substrate, the crystalline structure and adhesion of the film can be controlled.

Film Thickness Control: By monitoring the evaporation rate and time, the thickness of the film is precisely controlled using a quartz crystal monitor or an optical monitor. Thickness control is especially important for optical coatings and electronics manufacturing.

Cooling and Removal:

Cooling: Turn off the heaters and allow the substrate to cool to room temperature. Avoid contamination of the substrate surface during cooling.

Removal: Open the vacuum chamber and remove the coated substrate for subsequent processing or testing. The coated substrate is usually subjected to surface analysis and performance tests to ensure that the coating quality meets the requirements.

 

If you want to buy or have question please contact:

Cheer

Email: Cheer@cysitech.com

Tel:+86 18721621007

WhatsApp: +86 18721621007

WeChat: 18721621007

Name

Nb2O5

Chemical Formula

Nb2O5

Specifications

1-2/1-3/mm

Melting point

1530

Evaporator source

E

Refractive index

2.3

Transparent band

200-9000nm

Usage

Anti-reflection film, interference   filter, etc


Contact Us
  • E-mail: cysi@cysi.wang
  • Tel: +86 371 5519 9322
  • Fax: +86 371 8603 6875
  • Add: No. 820, 8th Floor, 1st Unit, 9th Block, Cuizhu Street, High-Tech Zone, Zhengzhou, Henan, China




Follow Us

Copyright © Zhengzhou CY Scientific Instrument Co., Ltd. All Rights Reserved    Update cookies preferences

| Sitemap |       Technical Support: